PA66 塑膠原料1300G 增強級 日本旭化成 耐疲勞抗蠕變

Physical Properties物理性質

Metric公制數據

English英制數據

Comments測試方法

Specific Gravity比重

1.39g/cc

1.39g/cc

Dry; ASTM D792

Water Absorption吸水率

1.7 %

1.7 %

Wet

Linear Mold Shrinkage線性收縮率

0.0040cm/cm

0.0040in/in

Dry; ASTM D2863

Linear Mold Shrinkage, Transverse線性收縮率/橫向

0.0090cm/cm

0.0090in/in

Dry; ASTM D2863

Mechanical Properties力學性能

Metric公制數據

English英制數據

Comments測試方法

Hardness, Rockwell M羅氏硬度M

75

75

Wet; ASTM D785

96

96

Dry; ASTM D785

Hardness, Rockwell R羅氏硬度R

112

112

Wet; ASTM D785

120

120

Dry; ASTM D785

Tensile Strength, Yield屈服拉伸強度

132MPa

19100psi

Wet; ASTM D638

186MPa

27000psi

Dry; ASTM D638

Elongation at Break斷裂伸長率

3.0 %

3.0 %

Dry; ASTM D638

5.0 %

5.0 %

Wet; ASTM D638

Flexural Strength彎曲強度

216MPa

31300psi

Wet; ASTM D790

289MPa

41900psi

Dry; ASTM D790

Flexural Modulus彎曲彈性模量

6.30GPa

914ksi

Wet; ASTM D790

9.30GPa

1350ksi

Dry; ASTM D790

Izod Impact, Notched懸臂梁缺口沖擊強度

1.27J/cm

2.38ft-lb/in

Dry; ASTM D256

1.47J/cm

2.75ft-lb/in

Wet; ASTM D256

Taber Abrasion, mg/1000 Cycles周期泰伯磨耗

15

15

Wet; ASTM D1044

Thermal Properties熱性能

Metric公制數據

English英制數據

Comments測試方法

CTE, linear線性熱膨脹系數

30.0μm/m-°C@Temperature 20.0 °C

16.7μin/in-°F@Temperature 68.0 °F

Dry; ASTM D696

Specific Heat Capacity比熱容

1.59J/g-°C

0.380BTU/lb-°F

Dry

Thermal Conductivity導熱系數

0.300W/m-K

2.08BTU-in/hr-ft2-°F

Dry

Deflection Temperature at熱變形溫度0.46 MPa (66 psi)

260°C

500°F

Dry; ASTM D648

Deflection Temperature at熱變形溫度1.8 MPa (264 psi)

250°C

482°F

Dry; ASTM D648

Flammability, UL94阻燃等級

HB

HB

Dry

Oxygen Index氧指數

23 %

23 %

Dry; ASTM D2863