pa6性能參數 pa6+gf30
pa61010c2 G6071
G6357 pa6+20%gf
pa6gf30價格多少 pa6+15%gf
UBE Nylon 1013B Good Abrasion Resistance; Good Chemical Resistance
UBE Nylon 1015 GNKF Good Flow; Good Moldability; Good Surface Finish; Weldable
UBE Nylon 1015 UC2 Good Moldability; Good Surface Finish
UBE Nylon 1015GC6 Good Abrasion Resistance; Good Chemical Resistance
UBE Nylon 1015GC9 Metal Replacement Good Abrasion Resistance; Good Chemical
UBE Nylon 1022 C2 Film Barrier Resin; Food Contact Acceptable
UBE Nylon 1022 FDX99 Film Good Processability; High Clarity; Low Slip
UBE Nylon 1022 MT2 Monofilaments Good Flexibility; Good Processability
UBE Nylon 1022 T Monofilaments Good Processability; High Clarity
UBE Nylon 1022B Monofilaments Good Abrasion Resistance; Good Chemical
UBE Nylon 1024JI Fuel Lines Fuel Resistant; Good Processability; High Impact
UBE Nylon 1030 B Film; Sheet; Tubing Food Contact Acceptable; General Purpose
編輯本段應用范圍
工業生產中泛用于制造軸承、圓齒輪、凸輪、傘齒輪、各種滾子、滑輪、泵葉輪、風扇葉片、蝸輪、
推進器、螺釘、螺母、墊片、高壓密封圈、耐油密封墊片、耐油容器、外殼、軟管、電纜護套、剪切機
滑輪套、牛頭刨床滑塊、、電磁分配閥座、冷陳設備、襯墊、軸承保持架、汽車和拖拉機上各種輸油管、
活塞、繩索、傳動皮帶，紡織機械工業設備零霧料，以及日用品和包裝薄膜等。
編輯本段加工工藝
干燥處理：
由于PA6很容易吸收水分，因此加工前的干燥特別要注意，如果材料是用防水材料包裝供應的，則容
器應保持密閉。如果濕度大于0.2%，建議在80℃以上的熱空氣中干燥16小時。如果材料已經在空氣中暴
露超過8小時，建議進行溫度為105℃，8小時以上的真空烘干。
融化溫度：
230-280℃，對于增強品種為250-280℃。
模具溫度：
80-90℃。模具溫度很顯著地影響潔凈度，而潔凈度又影響著塑件的機械特性。對于結構部件來說結晶
度很重要，因此建議模具溫度為80-90℃。對于薄壁的、流程較長的塑件也建議施用較高的模具溫度。增
大模具溫度可以提高塑件的強度和剛度，但卻降低了韌性。如果壁厚大于3mm，建議使用20-40℃的低溫
模具。對于玻璃纖維增強材料模具溫度應大于80℃。
注射壓力：
一般在750-1250bar之間（取決于材料和產品設計）
注射速度：
高速（對增強材料要稍微降低）
流道和澆口：
對于PA6的凝固時間很短，因此澆口的位置非常重要。澆口孔徑不要小于0.5*T（這里T為塑件的厚度）。
如果使用熱流道，澆口尺寸應比使用常規流道小一些，因為熱流道能夠幫助阻止材料過早凝固。如果用潛入
式澆口，澆口的Zui小直徑應當是0.75mm。
編輯本段化學和物理特性
PA6的化學物理特性和PA66很相似，然而，它的熔點較低，而且工藝溫度范圍很寬。它的抗沖擊性和抗
溶解性比PA66要好，但吸濕性也更強。因為塑件的許多品質特性都要受到吸濕性的影響，因此使用PA6設計
產品時要充分考慮這一點。為了提高PA6的機械特性，經常加入各種各樣的改性劑。玻璃纖維就是Zui常見的
添加劑，有時為了提高抗沖擊性還加入合成橡膠，如EPDM和SBR等。對于沒有添加劑的產品，PA6的收縮
1%到1.5%之間。加入玻璃纖維添加劑可以使收縮率降低到0.3%（但和流程相垂直的方向還要稍高一些）。
成型組裝的收縮率主要受材料的結晶度和吸濕性影響。實際的收縮率還和塑件設計、壁厚及其它工藝參數成
函數關系。
PA6與PA66區別