Plexiglas 6NPlexiglas 7HPlexiglas 7MPlexiglas 7NPlexiglas 8HPlexiglas 8NPlexiglas Heatresist FT15Plexiglas Heatresist hw55Plexiglas Heatstop 8N blackPlexiglas Hi-Gloss NTA-1Plexiglas Hi-Gloss NTA-3Plexiglas LED 8N LD12Plexiglas LED 8N LD24Plexiglas LED 8N LD48Plexiglas LED 8N LD96Plexiglas LED white 0V200Plexiglas LED white 0V606Plexiglas Optical POQ62Plexiglas Optical POQ64Plexiglas Optical POQ66Plexiglas Resist zk20Plexiglas Resist zk30Plexiglas Resist zk40Plexiglas Resist zk4BRPlexiglas Resist zk4HCPlexiglas Resist zk50Plexiglas Resist zk5BRPlexiglas Resist zk5HCPlexiglas Resist zk5HFPlexiglas Resist zk6BRPlexiglas Resist zk6HCPlexiglas Resist zk6HFPlexiglas Satinice df20 8NPlexiglas Satinice df21 8NPlexiglas Satinice df22 7HPlexiglas Satinice df22 7NPlexiglas Satinice df22 8NPlexiglas Satinice df22 zk6BRPlexiglas Satinice df23 7HPlexiglas Satinice df23 7NPlexiglas Satinice df23 8NPlexiglas Satinice df23 zk6BRPlexiglas Satinice df33 7H

亞克力PMMA無明顯熔點，160°開始軟化，180°可以流動，分解溫度為270°。注塑溫度的可調區間比較大。注塑時，一般使用溫度為180℃--240℃；它吸少量水分，生產時，需烘干。
先分析一下氣泡形成的原因：內部有氣泡無外乎兩種情況：1，塑料收縮，當注塑壓力保壓壓力不適當時，制品密度不夠高，材料在收縮過程中，因溫度冷卻是由外至內的，內部更容易被收縮成空洞形成狀似氣泡的東西。2，注塑螺桿中的氣體被填充進模具型腔時，這股氣體不能排出型腔聚集在材料內部。產生氣體的原因一般有:1,料溫過高或高溫下儲料時間過長，材料發生氣化產生氣體。2，塑料中的添加劑一般耐溫較低，在高溫下首先發生分解氣化。3，原料干燥不夠，含有水分，水分氣化。
所以，按上述的適合的溫度加工，降低料溫，提高模溫，降低注塑速度，增加保壓壓力，延長烘料時間這些措施都可以改善氣泡的問題。